Release of corrsive substances |
CT (as per EN 13813) |
---|---|
Compressive strength class |
C30 (as per EN 13813) |
Compressive strength average |
35 MPa (as per EN 13813) |
Flexural strength class |
F7 (as per EN 13813) |
Flexural strength average |
8 MPa (as per EN 13813) |
Fire resistance class |
A1fl (as per EN 13813) |
RWFC |
550 (as per EN 13813) |
Adhesion to surface |
B1,5 (as per EN 13813) |
Thickness 1 |
3–30 mm |
Thickness 2 |
6–10 mm on lightweight concrete |
Grain size |
< 1 mm |
Material consumption |
1.6 kg/m²/mm |
Weight (dry state) |
1600 kg/m³ |
Water requirements |
4,2 l/20 kg |
Flow rate |
max 145 mm |
Workplace temperature |
10–25 °C |
Mixing time |
3 min |
Working time |
10–25 min |
Final set |
1–3 hrs |
Coverable (tiles) |
12 hrs |
Carpetable |
12–24 hrs |
pH |
approx. 11 |
Water damage resistant |
yes |
Surface Tensile Bond Strength, 28 days (sanded, loaded surface) |
> 1.5 MPa |
Shrinkage |
0.03–0.05 % |
TVOC 28 days |
30 μg/(m² h) |